- News
- Books
Featured Books
- design007 Magazine
Latest Issues
Current IssueLevel Up Your Design Skills
This month, our contributors discuss the PCB design classes available at IPC APEX EXPO 2024. As they explain, these courses cover everything from the basics of design through avoiding over-constraining high-speed boards, and so much more!
Opportunities and Challenges
In this issue, our expert contributors discuss the many opportunities and challenges in the PCB design community, and what can be done to grow the numbers of PCB designers—and design instructors.
Embedded Design Techniques
Our expert contributors provide the knowledge this month that designers need to be aware of to make intelligent, educated decisions about embedded design. Many design and manufacturing hurdles can trip up designers who are new to this technology.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - design007 Magazine
Material Witness: Using Scaled Flow Data
September 16, 2015 | Chet GuilesEstimated reading time: 5 minutes
The IPC TM-650 Scaled Flow Test (2.4.38) uses three values to determine pressed thickness and flow of a given resin system: Ho (the theoretical value of a pressed sample assuming no air entrainment and no flow calculated from the weight of the test stackup), Hf (the actual final thickness per ply measured by micrometer after the flow test) and ΔH (the difference between Ho and Hf expressed in mils of thickness change).
Based on work done originally by Bartlett, Bloechele and Mazeika at Bell Labs in New Jersey [1] and discussed in relation to specific grades of epoxy prepreg by Del, Marx and Sallo of Fortin Laminating [2], scaled flow has long been used in the industry for characterizing epoxy prepregs used for manufacturing multilayer PWBs.
The scaled flow test depends on understanding the Integrated Flow Value for a prepreg system, which can be expressed as
Flow ~ C * (P/A) * Integral (1/η) (from time 0 to ∞)
Where: C is a constant for the particular resin system determined empirically
(P/A) is the ratio of pressure (psi) to area (in2)
Integral (1/η) is the integral of 1/viscosity (poise) taken over the melt, flow and cure cycle
The flow at any given moment is inversely proportional to the viscosity, so the integral takes into account the changing viscosity as the resin first melts and then starts to cure. The ΔH value of the scaled flow test is a measure of the integrated flow during the entire test, and as we will see, the flow of prepreg during MLB fabrication can be controlled by taking this ΔH value into consideration.
The basic scaled flow test uses either 10 plies 5.5” x 7” for heavier glass fabrics such as 2113, 2116, etc. or 18-20 plies for lightweight glass fabrics such as 106 and 1080. These stacks are designed to provide approximately equal masses of material regardless of glass style to normalize the test parameters. (A substantially heavier stack would heat up unevenly and more slowly, and a substantially lighter stack would heat up too fast and give doubtful results.)
The stack weights are used to calculate Ho based on the glass weight and density as well as the resin weight and density. The original scaled flow test was based on conventional FR-4 epoxy whose resin density was approximately 1.35. Nominal values of glass weight and density and resin weight and density are used for doing the calculation of Ho based on actual stack weight.
Resin systems whose density is not very near 1.35 do not quite fit into the official IPC test method because all the stack weight data used assumes epoxy resin of a standard 1.35 density. Any resin whose density varies from that value requires a new set of calculated weights for various stack-ups in order to provide precise data. This is especially true of filled systems whose resin density now includes a ceramic component as well as the organic resins themselves and may have densities higher than standard. For example, a filled polyimide resin whose density is 1.41 would appear to be pressing too thin if the Ho was calculated based on epoxy calculations at 1.35; and conversely, a polyimide system whose resin density was 1.30 (because of low or no Bromine content) would seem to be pressing too thick if calculations were performed based on a standard epoxy at density 1.35. I mention this because there is a tendency to use the IPC method as if the table of basis weights is gospel, while in fact it is only valid for resin systems whose density is that of standard FR-4.
Because our primary interest is in final pressed thickness, scaled flow testing provides a useful tool for making first order approximations of this critical value, and also provides a useful value (ΔH) for adjusting pressure to achieve desired levels of flow.
This relationship can be expressed roughly as:
P = k * (1/ ΔH) * A * [√(W)/ √(L)]
Where: k is a constant based on the resin system and units (~1 for conventional polyimide systems)
(1/ ΔH) is the reciprocal of the ΔH value from the scaled flow test
A is the area of the MLB being pressed
[√(W)/ √(L)] is a “shape factor” using the ratio of the square roots of the width and length
An 18 x 12 lamination size with a k of 1.0 gives the following data. As you can see in Figure 1, at ΔH 0.5 the laminating pressure is about 350 psi, which can be adjusted as needed for a particular design, or reduced somewhat if vacuum lamination is used, and so forth. The point is that with a normal range of ΔH = 0.4 to 0.8 you can quickly see how to adjust pressure to compensate for any flow issues. At very low values of ΔH, the pressure requirement to achieve adequate flow will rise rapidly – as might be the case with out of date prepreg, or low-flow prepreg if flow and fill becomes critical.
Figure 1: Graph showing laminating pressure vs ΔH value for polyimide.
The use of scaled flow has another hidden benefit for thickness control. By using a weight standard rather than a traditional resin content test, any variation in the basis weight of the glass fabric is minimized. Because the density of resin is roughly half that of glass, any change in glass weight will require about double that increase to keep resin content “in spec,” which can result in too thick a pressed thickness per ply. Conversely, if the glass basis weight runs low, reducing resin to achieve the “spec percentage” can result in a laminate that will press too thin.
With pressed ply thickness critical to electrical properties such as impedance (Zo) and to overall board thickness, use of a scaled flow standard based on weight and ΔH results in a tighter control of thickness than would otherwise be achieved. Now some might say this is a small difference, and it may well be in most cases, but when you are building 15-25 layer MLBs, with two or more pieces of prepreg between each inner layer detail, tolerance variations can add up quickly.
Arlon is using a scaled flow method internally to control weights and flows for its lamination grade prepregs with the result that in the past year we have made significant improvements in laminate thickness variability. In newer products such as filled laminates and prepregs, scaled flow would be the material specification of choice for calling our thickness and flow.
Hoping that this brief overview will help those of you who have not been using scaled flow for many years to appreciate the benefits this method can confer. With summer 2015 behind us, this is the Material Witness wishing all a Happy Autumn!
Chet Guiles is a consultant for Arlon Electronic Materials.
Suggested Items
Real Time with... IPC APEX EXPO 2024: Looking Back, Looking Forward With IEC
04/19/2024 | Real Time with...IPC APEX EXPOIEC came to the RTW booth and discussed both the legacy of IEC's past and the vision for its future. Industry veteran Bruno Ferri highlighted his quarter-century tenure in the industry and with IEC since its founding. He still exhibits boundless enthusiasm for the industry. Brando Stone, a young professional and a future face of IEC, talked about IEC's plans going forward and his experience at this year's IPC APEX EXPO.
I-Connect007 Editor’s Choice: Five Must-Reads for the Week
04/19/2024 | Marcy LaRont, PCB007 MagazineFor my must-read picks of the week, I’m highlighting Parker Capers, a young professional seeking employment, solid counsel from Dan Beaulieu on what your post-show plan should look like, more information and insight on “chiplets” and the need for secure data transfer standards from columnist Preeya Kuray, as well as Matt Stevenson’s design for reality wisdom. It’s a reminder to download one of our newest books (there are several) you don't want to miss if you are an assembler.
Real Time with... IPC APEX EXPO 2024: Exploring IPC's PCB Design Courses with Kris Moyer
04/18/2024 | Real Time with...IPC APEX EXPOGuest Editor Kelly Dack and IPC instructor Kris Moyer discuss IPC's PCB design training and education offerings. They delve into course topics such as design fundamentals, mil/aero, rigid-flex, RF design, and advanced design concepts. They also highlight material selection for high-speed design, thermal management, and dissipation techniques. The interview wraps up with details about how to access these courses online.
IPC Bestows Posthumous Hall of Fame Award to Industry Icon Michael Ford
04/18/2024 | IPCIPC honored the late Michael Ford, Aegis Software, for his extraordinary contributions to the global electronics manufacturing industry with the IPC Raymond E. Pritchard Hall of Fame Award at IPC APEX EXPO 2024. IPC’s most prestigious honor, the Hall of Fame Award is given to individuals who have provided exceptional service and advancement to IPC and the electronics industry. Ford, an industry leader and valued IPC volunteer, died suddenly in January 2024.
Two Industry Rising Stars Recognized at IPC APEX EXPO 2024
04/17/2024 | IPCTwo of the industry’s best and brightest were presented with an IPC Rising Star Award at IPC APEX EXPO 2024 in recognition of their leadership roles and support of IPC standards, education, advocacy, and solutions to industry challenges. Award recipients were Naim Kapadia and Michael Schleicher.